Effect of Calcium Nitrate Treatment on the Structure and Mechanical Properties of Raw Silk

WANG Xin; LI Yi; LIU Qingsong; LI Xinning; XIA Qingyou; ZHAO Ping

doi:10.13718/j.cnki.xdzk.2022.08.009

2022 Volume 44 Issue 8

Article Contents

Previous Article Next Article

WANG Xin, LI Yi, LIU Qingsong, et al. Effect of Calcium Nitrate Treatment on the Structure and Mechanical Properties of Raw Silk[J]. Journal of Southwest University Natural Science Edition, 2022, 44(8): 77-84. doi: 10.13718/j.cnki.xdzk.2022.08.009

Citation:

WANG Xin, LI Yi, LIU Qingsong, et al. Effect of Calcium Nitrate Treatment on the Structure and Mechanical Properties of Raw Silk[J]. Journal of Southwest University Natural Science Edition, 2022, 44(8): 77-84. doi: 10.13718/j.cnki.xdzk.2022.08.009

Effect of Calcium Nitrate Treatment on the Structure and Mechanical Properties of Raw Silk

Biological Science Research Center, Southwest University/State Key Laboratory of Silkworm Genome Biology, Chongqing 400715, China

More Information

Corresponding author: ZHAO Ping
Received Date: 05/10/2021
Available Online: 20/08/2022
MSC: S881.3

Abstract

In order to explore whether salt shrinkage processing can improve the mechanical properties of raw silk fibers while improving the softness and comfort of raw silk fibers, different percentages of calcium nitrate solutions were used to treat raw silk fibers under different temperatures. By using scanning electron microscopy, polarized light microscopy, polyacrylamide gel electrophoresis, infrared absorption spectroscopy, and mechanical tests, the shrinkage rate, diameter, surface morphology, orientation, protein composition, secondary structure and mechanical properties of the raw silk fibers after treatment were systematically analyzed. The results showed that after calcium nitrate solution treatment, raw silk fiber swelled and shrank significantly. The good orientation of raw silk fiber was destroyed, and the proteins of raw silk fiber were degraded to a certain extent. These changes became more apparent as the calcium nitrate percentage and treatment temperature increasing. Furthermore, high percentage of calcium nitrate solution could change the secondary structure content and mechanical properties of raw silk fibers. After being treated with a 46.8% calcium nitrate solution at 65 ℃, the strain of the raw silk fiber increased to 39.1%. However, the stress reduced significantly.
- raw silk fiber,
- salt shrinkage processing,
- calcium nitrate,
- mechanical properties,
- structure analysis

References

[1]	杨伟克, 唐芬芬, 刘增虎, 等. 家蚕β-呋喃果糖苷酶基因BmSuc1表达特征及其对激素的响应[J]. 南方农业学报, 2021, 52(7): 1991-1997. doi: 10.3969/j.issn.2095-1191.2021.07.029 CrossRef Google Scholar
[2]	许瑾邵, 邵云华, 黄静怡, 等. 家蚕己糖激酶基因进化分析及其多转录本在胚胎早期发育过程中的表达特性[J]. 南方农业学报, 2021, 52(6): 1701-1708. doi: 10.3969/j.issn.2095-1191.2021.06.031 CrossRef Google Scholar
[3]	徐水, 胡征宇. 茧丝学[M]. 北京: 高等教育出版社, 2016. Google Scholar
[4]	ZHOU L, CHEN X, SHAO Z Z, et al. Effect of Metallic Ions on Silk Formation in the Mulberry Silkworm, Bombyx Mori[J]. The Journal of Physical Chemistry B, 2005, 109(35): 16937-16945. doi: 10.1021/jp050883m CrossRef Google Scholar
[5]	WANG X, LI Y, LIU Q S, et al. In Vivo Effects of Metal Ions on Conformation and Mechanical Performance of Silkworm Silks[J]. Biochimica et Biophysica Acta (BBA) - General Subjects, 2017, 1861(3): 567-576. doi: 10.1016/j.bbagen.2016.11.025 CrossRef Google Scholar
[6]	LIU Q S, WANG X, TAN X Y, et al. A Strategy for Improving the Mechanical Properties of Silk Fiber by Directly Injection of Ferric Ions into Silkworm[J]. Materials & Design, 2018, 146: 134-141. Google Scholar
[7]	WANG X, ZHAO P, LI Y, et al. Modifying the Mechanical Properties of Silk Fiber by Genetically Disrupting the Ionic Environment for Silk Formation[J]. Biomacromolecules, 2015, 16(10): 3119-3125. doi: 10.1021/acs.biomac.5b00724 CrossRef Google Scholar
[8]	周宏湘. 真丝绸的盐缩加工[J]. 丝绸, 1978, 15(11): 44. Google Scholar
[9]	刘辅庭. 运动服的动向[J]. 现代丝绸科学与技术, 2012, 27(4): 168-172. doi: 10.3969/j.issn.1674-8433.2012.04.015 CrossRef Google Scholar
[10]	董文秀, 李军生, 李秋杰, 等. 光谱法研究钙离子对丝素蛋白溶解过程中结构的影响[J]. 分析测试学报, 2014, 33(12): 1410-1415. doi: 10.3969/j.issn.1004-4957.2014.12.014 CrossRef Google Scholar
[11]	赵为陶, 林红, 陈宇岳. 金属离子在纺织领域的应用[J]. 苏州大学学报(工科版), 2006, 26(6): 1-5. Google Scholar
[12]	陈慰来, 普丹丹, 潘莲君. 桑蚕丝针织物盐缩工艺探讨[J]. 纺织学报, 2008, 29(1): 78-81. doi: 10.3321/j.issn:0253-9721.2008.01.020 CrossRef Google Scholar
[13]	YANG H Y, YANG S N, KONG J L, et al. Obtaining Information about Protein Secondary Structures in Aqueous Solution Using Fourier Transform IR Spectroscopy[J]. Nature Protocols, 2015, 10(3): 382-396. doi: 10.1038/nprot.2015.024 CrossRef Google Scholar
[14]	周文, 陈新, 邵正中. 红外和拉曼光谱用于对丝蛋白构象的研究[J]. 化学进展, 2006, 18(11): 1514-1522. doi: 10.3321/j.issn:1005-281X.2006.11.014 CrossRef Google Scholar
[15]	张国政, 李木望, 鲁成. 中国养蚕学[M]. 上海: 上海科学技术出版社, 2020. Google Scholar
[16]	陈宇岳, 盛家镛, 胡凤霞, 等. 真丝纤维在钙盐作用下的形态结构研究[J]. 纺织学报, 1999, 20(3): 140-142, 183. Google Scholar
[17]	林红, 陈宇岳. 钙盐处理对真丝纤维力学性能的影响[J]. 丝绸, 2003, 40(12): 33-35. doi: 10.3969/j.issn.1001-7003.2003.12.014 CrossRef Google Scholar
[18]	丁欢. 蚕丝在钙盐溶液中的超声分纤研究[J]. 中国纤检, 2019(9): 83-85. doi: 10.3969/j.issn.1671-4466.2019.09.025 CrossRef Google Scholar
[19]	DUBEY P, MURAB S, KARMAKAR S, et al. Modulation of Self-Assembly Process of Fibroin: an Insight for Regulating the Conformation of Silk Biomaterials[J]. Biomacromolecules, 2015, 16(12): 3936-3944. doi: 10.1021/acs.biomac.5b01258 CrossRef Google Scholar
[20]	QIU W, PATIL A, HU F, et al. Hierarchical Structure of Silk Materials Versus Mechanical Performance and Mesoscopic Engineering Principles[J]. Small, 2019, 15(51): 1903948. Google Scholar

Access History

通讯作者: 陈斌, bchen63@163.com

1.
沈阳化工大学材料科学与工程学院沈阳 110142

Figures(6) / Tables(1)

Export Citation

PDF

XML

Article Metrics

Article views(1291) PDF downloads(218) Cited by(0)

Access History

Other Articles By Authors

on this site
- WANG Xin
- LI Yi
- LIU Qingsong
- LI Xinning
- XIA Qingyou
- ZHAO Ping
on Google Scholar
- WANG Xin
- LI Yi
- LIU Qingsong
- LI Xinning
- XIA Qingyou
- ZHAO Ping

HTML

开放科学（资源服务）标志码（OSID）：
家蚕是世界上最重要的经济昆虫之一，也是支撑蚕丝产业的生物基础，具有极高的经济价值^[1-2]. 蚕丝是一种天然的蛋白纤维，具有良好的光泽、轻柔舒适的手感、适宜的吸水性、对人体肌肤的亲和性等特征，有“纤维皇后”的美称^[3]. 然而，蚕丝纤维由于其本身具有的弹性小、抗形变性差、易起皱泛黄等缺陷，导致以蚕丝纤维加工为主的丝绸产业受到了巨大的冲击. 在科技日益发展、人民生活水平不断提高的今天，蚕丝产业又面临着一系列新的挑战. 首先，近年来我国已经逐渐由生丝原料的最大出口国转变为世界最大丝绸终端商品生产国和出口国，这一产业结构的变化提示蚕丝产业应有效结合国内外消费者升级的需求，着力优化产品结构，提高生丝及其制品的品质，从而有效拓宽丝绸行业的生存空间. 其次，蚕丝还面临多种纤维竞争带来的挑战. 世界纺织科技迅猛发展，使得蚕丝不断受到其他低价合成纤维的冲击. 正因如此，改善蚕丝纤维性能，克服蚕丝固有缺陷，才能弥补蚕丝自身短板，开创出更多新的应用场景，提高蚕丝产品附加值，实现丝绸产业振兴.

为了克服蚕丝纤维弹性小和抗形变差等力学性能上的缺陷，本研究小组受蚕丝在家蚕丝腺中成纤维过程需要金属离子参与的启发，通过向家蚕注射金属离子的方式，实现了蚕丝纤维力学性能的改良^[4-6]. 进一步通过将金属离子结合蛋白在家蚕前部丝腺过表达，获得了力学性能提升的新型家蚕品种和蚕丝纤维素材^[7].

除利用注射、基因过量表达等体内操作的方式将金属离子导入蚕丝以改良蚕丝力学性能外，直接利用中性盐在高温条件下处理已经纤维化的蚕丝也是对蚕丝外观及性能改良的手段之一. 目前，比较成熟的加工方法是蚕丝的盐缩加工工艺. 将蚕丝织物或纤维在较高百分比的硝酸钙、氯化钙等中性盐的热溶液中进行处理，蚕丝或纤维会显著地收缩和卷曲，利用这种现象使蚕丝纤维及织物收缩，使之具有皱缩效果的加工，即盐缩加工^[8]. 盐缩加工处理的蚕丝能产生卷曲状的外观、蓬松的触感和别致的风格，从而改善蚕丝制品的手感，使其触感更加柔软^[9]. 产生这种现象的原因可能在于丝蛋白中酪氨酸、丝氨酸的侧链基团与钙离子发生配位作用形成螯合物，这个过程中破坏了维持丝蛋白原有结构的部分氢键和范德华力，从而使纤维溶胀、分子结构松弛^[10-11]. 目前，关于盐缩加工的相关研究主要集中在对其工艺优化及处理后纤维和织物表面形态的变化方面，取得了一定的成果，如陈蔚来等^[12]对蚕丝织物盐缩工艺进行了探讨，发现硝酸钙溶液在百分比为46.8%，温度为65 ℃，时间为12 min时处理蚕丝盐缩效果最好，并且对蚕丝的损伤也较小. 但是，对于盐缩加工后蚕丝纤维结构和性能是如何变化的相关研究还相对较少.

基于以上背景，本文参考陈蔚来等^[12]的加工条件，采用不同百分比和不同温度的硝酸钙溶液对生丝纤维进行盐缩处理. 对处理后的茧丝形貌、取向、蛋白质组分、结构和力学性能进行系统研究，旨在探究盐缩加工处理在提高生丝纤维柔软度和舒适性的同时能否改良生丝纤维的力学性能，并对蚕丝盐缩加工工艺进行探讨.

1. 材料与方法

1.1. 实验材料

生丝纤维(优级白厂丝，规格20/22)购自四川南充六合制丝有限责任公司，四水合硝酸钙、溴化锂、尿素均为AR级，购自上海生工生物工程股份有限公司，溴化钾购自上海阿拉丁生化科技股份有限公司，去离子水购自美国Sigma-Aldrich公司，十二烷基磺酸钠—聚丙烯酰胺电泳(SDS-PAGE)梯度预制胶(4%~16%)、电泳缓冲液、上样缓冲液、预染蛋白质分子量标准、考马斯亮蓝R250染色液及脱色液均购自美国ThermoFisher Scientific公司.

1.2. 实验仪器

BJ-1000C型电子天平(瑞士普利赛斯)、DHG-9140A型电热恒温鼓风干燥箱(上海齐欣科学仪器有限公司)、蛋白质电泳系统(美国ThermoFisher Scientific)、DM2700P型偏光显微镜(德国徕卡)、扫描电子显微镜(日本日立)、Nicolet iN10型傅里叶变换红外光谱仪(美国ThermoFisher Scientific)、AG-X plus型万能测试仪(日本岛津).

1.3. 硝酸钙盐缩处理

先将生丝纤维在去离子水中清洗并自然风干，按照表 1中所示的百分比利用去离子水配制硝酸钙溶液. 准确量取100 mm长度的生丝纤维，将其按照表 1实验条件进行硝酸钙盐缩处理12 min. 取处理后的生丝纤维，利用去离子水冲洗5次，每次2 min，室温晾干后进行长度测量，计算收缩率.

1.4. 形貌观察

将处理后的生丝纤维剪成10 mm长度，平整地粘贴在扫描电镜专用导电胶带上，镀金5 min后进行扫描电镜观察. 随机选择3个区段，利用图像处理软件测量其直径，并进行拍照. 另取处理后的生丝纤维，将其固定于载玻片上后，置于偏光显微镜下观察、拍照.

1.5. 十二烷基硫酸钠-聚丙烯酰胺凝胶电泳(SDS-PAGE)分析

取处理后的生丝纤维，剪刀剪碎后称取10 mg，向其中加入500 μL的9.6 mol/L溴化锂溶液，待丝纤维溶解后，10 000 r/min离心5 min，取上清液. 将170 μL的8 mol/L尿素和30 μL上清溶液混合，加入50 μL蛋白上样缓冲液，室温静置2 h后，取10 μL进行SDS-PAGE，100 V恒压电泳. 电泳结束后进行考马斯亮蓝染色.

1.6. 傅里叶变换红外光谱(FTIR)分析

随机选取处理后的生丝纤维(样本数n=5)，剪碎后将其与研磨后的溴化钾粉末混合，压片后放入FTIR分析仪载物台. 调节红外线光斑，将其聚焦到样品上进行扫描. 扫描范围设为500 cm^-1至2 000 cm^-1，光谱分辨率为0.1 cm^-1，每个样品扫描次数为64次. 每次样品扫描前需先采集背景. 获得谱图后利用OMNIC 9软件进行自动基线校正. 提取酰胺Ⅰ区域(1 720 cm^-1至1 580 cm^-1)峰图，利用PeakFit软件(版本号4.12)将酰胺Ⅰ区域谱图进行分峰，按照文献[13-14]方法识别蚕丝中二级结构特征峰，提取每一个特征峰的峰面积，最后将数据导出.

1.7. 生丝纤维力学性能测试

拉伸实验在25 ℃，30%相对湿度的条件下进行. 测试仪器为装配有50 N感应模具的万能测试仪，拉伸速度为2 mm/min. 仪器自动记录茧丝的载荷和位移，直至茧丝断裂. 实验结束后利用Advantage软件计算生丝纤维的应力、应变等力学性能数据. 利用应力、应变数据在Origin软件(版本号8.0)中绘制应力—应变曲线，并拟合出平均曲线(样本数n＞30).

3. 结论

本研究系统地调查了不同温度和不同百分比的硝酸钙处理生丝纤维后形貌、取向、蛋白质分子组分、结构和力学性能的变化情况，得出以下结论：

1) 硝酸钙溶液处理后，生丝发生明显的溶胀和收缩，生丝纤维的良好取向被破坏，其蛋白质组分发生降解，且这种效果随着硝酸钙百分比及处理温度的增加越发明显.

2) 硝酸钙溶液处理可改变生丝纤维二级结构比例和力学性能. 在高温处理下生丝纤维的应力随硝酸钙溶液百分比增加而显著降低，应变显著增大. 使用百分比为46.8%的硝酸钙溶液在65 ℃条件下处理生丝纤维12 min可使纤维应变提高到39.1%.

3) 盐缩加工处理虽能提高生丝纤维弹性、柔软度和舒适性，但并不适合应用于以强度提升为目的的性能改良. 由于高强度的处理会使丝纤维蛋白质降解，结晶度下降，故应该根据蚕丝产品的最终需求，有效地控制好盐缩加工的工艺和方法.

Figure (6) Table (1) Reference (20)

Name
	Name cannot be empty!
E-mail
	Mailbox cannot be empty! Mailbox cannot be empty!
Telephone
	Mobile number cannot be empty! Please enter a valid mobile number!
Title

Content
Verification Code

Message Board